PVDF - Polyvinylidene Fluoride
LEGEND
A = amorphous - Cr = crystalline - C = clear - E = excellent - G = good - P = poor - O = opaque - T = translucent-
R = Rockwell - S = Shore
STRUCTURE: Cr
SPECIFIC DENSITY: 1.77
WATER ABSORBTION RATE (%): 0.03
ELONGATION (%): 50
TENSILE STRENGTH (psi): 5800
COMPRESSION STRENGTH (psi): 10000
FLEXURAL STRENGTH (psi): 7800
FLEXURAL MODULUS (psi): 260000
IMPACT (IZOD ft. lbs/in): 6.6
HARDNESS: R95
FABRICATION
- BONDING: P
- ULTRASONIC WELDING: P
- MACHINING: EG
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 300
- @ 264 psi: 190
UTILZATION TEMPERATURE (deg. F)
- min: -40
- max: 310
MELTING POINT (deg. F): 340
COEFFICIENT OF EXPANSION: 0.000022
ARC RESISTANCE: 60
DIELECTRIC STRENGTH (kV/mm): 22
TRANSPARENCY: T
UV RESISTANCE: G
CHEMICAL RESISTANCE
- ACIDS: P
- ALKALIS: G
- SOLVENTS: